Полипропилен H 388 F
Гомополимер. Для производства пленок методом литья под давлением и методм выдувки с охлаждением водой..

TIPPLEN H 388 F is a homopolymer polypropylene with a high slip and antiblock agent content. The product shows excellent processability in extrusion applications. TIPPLEN H 388 F a newly developed for high speed extrusion of transparent cast and blown film . This grade is suitable for the extrusion of low thickness films and can be used for film from 10 - 150 µm. Typical application include the extrusion of cast and blown film for quality packaging of foodstuffs such as pasta, snack, bakery products and confectionary. Other application include film for packaging for flowers, books, stationery and textile goods. The product complies with FDA, BGA and EU norms.

Properties

Standard method

Unit

Value

MFI (2.16 kg/230 °C)

ISO 1133

g/10 min.

9 (8.5-10.5)

Tensile strength at yield

ISO 527

N/mm 2

33

Elongation at yield

ISO 527

%

12

HDT - 0.46 N/mm 2

ISO 75

°C

95

Rockwell hardness

ISO 2039/2

R scale

88

Flexural modulus of elasticity (drawn)

ISO 527

N/mm 2

1300

Izod impact strength (notched, +23 °C)

ISO 180/1A

kJ/m 2

4

• MFI measured at 230 °C under a load of 2.16 kg with standard nozzle having a diameter of 2.095 mm.
• Average mechanical property values of several measurements carried out on standard injection moulded specimens (ISO 3167) conditioned at room temperature (ISO 291).