Полипропилен H 116 F
Гомополимер. Для переработки методом литья под давлением

TIPPLEN H 116 F is a high melt flow homopolymer polypropylene grade for low denier BCF, CF and staple fibers from medium to high spinning speeds. The product offers high homogenity, stable extrusion and excellent processability. TIPPLEN H 116 F is widely used for the production of bulked continuous filament for carpet face yarns. Another major application is production of high tenacity continuous filament. Continuous filament with medium tenacity is used for upholstery and sportswear. TIPPLEN H 116 F is suitable for the production of containers, household and kitchen articles, toys. This grade is an excellent polymer base for compounding and master batches. TIPPLEN H 116 F is suitable for food contact. The product complies with FDA and BGA norms.

Properties

Standard method

Unit

Value

MFI 21.6 N / 230 °C

 

ISO 1133

g / 10 min

25

ASTM D 1238

 

(21.2-28.8)

Tensile strength at yield

ISO 527

N/mm 2

36

ASTM D 638

 

36

Elongation at yield

ISO 527

%

10

ASTM D 638

 

9

HDT - 0.46 N/mm 2

ISO 75

°C

95

ASTM D 648

 

 

Rockwell hardness

 

ISO 2039/2

R scale

100

ASTM D 785

 

95

Flexural modulus

Drawn

ISO 527

N/mm 2

1650

of elasticity

Bent

ASTM D 790

N/mm 2

1550

Izod impact strength + 23 °C

ISO 180/1A

kJ / m 2

2.0

 

ASTM D 256

J / m

22

•  MFI measured at 230 °C under a load of 2.160 kg with standard nozzle having a diameter of 2.095 mm.
•  Typical mechanical property values measured on standard injection moulded specimens (ASTM D 2146 and ISO 3167), conditioned at room temperature (ASTM D 618 procedure A and ISO 291).